铁：即硅与铁的合金，按含硅量有45%、65%、75%和90%多种品级。 碳硅分析仪器硅铁牌号：硅铁按硅及其杂质含量，分为十六个牌号，其化学成分如下表：(根据GB2277-87) 牌号化学成分%
|
|
Si
|
Al
|
Ca
|
Mn
|
Cr
|
P
|
S
|
C
|
|
范围 不大于
|
|
|
|
|
|
|
|
|
|
FeSi90Al1.5
|
87.0-95.0
|
1.5
|
0.5
|
0.4
|
0.2
|
0.04
|
0.02
|
0.2
|
|
FeSi90Al3
|
87.0-95.0
|
3.0
|
0.5
|
0.4
|
0.2
|
0.04
|
0.02
|
0.2
|
|
FeSi75Al10.5-A
|
74.0-80.0
|
0.5
|
1.0
|
0.4
|
0.3
|
0.035
|
0.02
|
0.1
|
|
FeSi75Al10.5-B
|
72.0-80.0
|
0.5
|
1.0
|
0.5
|
0.5
|
0.04
|
0.02
|
0.2
|
|
FeSi75Al1.0-A
|
74.0-80.0
|
1.0
|
1.0
|
0.4
|
0.3
|
0.035
|
0.02
|
0.1
|
|
FeSi75Al1.0-B
|
72.0-80.0
|
1.5
|
1.0
|
0.5
|
0.5
|
0.04
|
0.02
|
0.2
|
|
FeSi75Al1.5-A
|
74.0-80.0
|
1.5
|
1.0
|
0.4
|
0.3
|
0.035
|
0.02
|
0.1
|
|
FeSi75 Al1.5-B
|
72.0-80.0
|
1.5
|
1.0
|
0.5
|
0.5
|
0.04
|
0.02
|
0.2
|
|
FeSi75 Al12.0-A
|
74.0-80.0
|
2.0
|
1.0
|
0.4
|
0.3
|
0.035
|
0.02
|
0.1
|
|
FeSi75 Al12.0-B
|
72.0-80.0
|
2.0
|
1.0
|
0.4
|
0.3
|
0.04
|
0.02
|
0.1
|
|
FeSi75 Al12.0-C
|
74.0-80.0
|
2.0
|
-
|
0.5
|
0.5
|
0.04
|
0.02
|
0.2
|
|
FeSi75-A
|
72.0-80.0
|
-
|
-
|
0.4
|
0.3
|
0.035
|
0.02
|
0.1
|
|
FeSi75-B
|
74.0-80.0
|
-
|
-
|
0.4
|
0.3
|
0.04
|
0.02
|
0.1
|
|
FeSi75-C
|
72.0-80.0
|
-
|
-
|
0.5
|
0.5
|
0.04
|
0.02
|
0.2
|
|
FeSi65
|
65.0-72.0
|
-
|
-
|
0.6
|
0.5
|
0.04
|
0.02
|
-
|
|
FeSi45
|
40.0-47.0
|
-
|
-
|
0.7
|
0.5
|
0.04
|
0.02
|
-
|
物理状态：硅铁浇注厚度，FeSi75系列各牌号硅铁锭不得超过100毫米;FeSi65锭不得超过80毫米。硅的偏析不大于4%。大粒度：50-350mm，中粒度：20-200mm，小粒度：10~100mm，*小粒度：10-50mm，其中小粒度占90%以上。 包装：硅铁根据需方要求，可采用散装、集装箱、袋装等形式发货。采用袋装或集装箱包装时，包装外面应有明显标志。
硅铁冶炼：硅铁是以焦炭、钢屑、石英(或硅石)为原料，用电炉冶炼制成的。炼制硅铁时，是将硅从含有SiO2的硅石中还原出来。碳硅分析仪器冶炼硅铁大多使用冶金焦作还原剂，钢屑是硅铁的调节剂。